Structures by: Isnard O.
Total: 130
Ce2Fe17
Ce2Fe17
Journal of the Less-Common Metals (1990) 162, 273-284
a=8.632Å b=8.632Å c=12.535Å
α=90° β=90° γ=120°
Ho1.9 Fe16.8
Fe16.8Ho1.9
Journal of the Less-Common Metals (1990) 162, 273-284
a=8.413Å b=8.413Å c=8.294Å
α=90° β=90° γ=120°
Fe10.2Mo1.8Nd
Fe10.2Mo1.8Nd
Journal of Alloys Compd. (1993) 191, 233-238
a=8.5952Å b=8.5952Å c=4.7908Å
α=90° β=90° γ=90°
Fe10.4Mo1.6Y
Fe10.4Mo1.6Y
Journal of Alloys Compd. (1993) 191, 233-238
a=8.5336Å b=8.5336Å c=4.782Å
α=90° β=90° γ=90°
Y Cu O2.5
CuO2.5Y
Solid State Sciences (2006) 8, 457-461
a=6.1869Å b=11.2066Å c=7.1484Å
α=90° β=90° γ=90°
Thorium iron carbide (2/17/0.8)
Fe17Th2
Journal of Alloys Compd. (1992) 186, 135-145
a=8.650(1)Å b=8.650(1)Å c=12.494(2)Å
α=90° β=90° γ=120°
Yttrium iron molybdenum nitride (1/10.1/1.9/0.8)
Fe10.12Mo1.88N0.8Y
Journal of Alloys Compd. (1993) 191, 233-238
a=8.6648(6)Å b=8.6648(6)Å c=4.8012(5)Å
α=90° β=90° γ=90°
Neodymium iron boride hydride (2/14/1/1.86)
BFe14H1.86Nd2
Journal of Applied Physics (1995) 78, 3 1892-1898
a=8.869Å b=8.869Å c=12.294Å
α=90° β=90° γ=90°
Nb Fe6 Ge6
Fe6Ge6Nb
Solid State Communications (2000) 114, 91-96
a=5.01Å b=5.01Å c=8.013Å
α=90° β=90° γ=120°
Tb Ti Ge
GeTbTi
Journal of Magnetism and Magnetic Materials (2001) 234, 261-273
a=4.039Å b=4.039Å c=7.635Å
α=90° β=90° γ=90°
(La2 Mo2 O9)0.889
La1.778Mo1.778O8.001
Chemistry of Materials (1,1989-) (2000) 12, 2575-2580
a=7.2014Å b=7.2014Å c=7.2014Å
α=90° β=90° γ=90°
Chevrel phase
MgMo6Se8
Chemistry of Materials (2006) 18, 16 3705
a=6.7435(3)Å b=6.7555(4)Å c=6.7608(4)Å
α=91.221(4)° β=94.288(4)° γ=94.443(5)°
Chevrel phase
MgMo6S8
Chemistry of Materials (2006) 18, 23 5492
a=9.4592714(6)Å b=9.4592714(6)Å c=10.5588446(5)Å
α=90.00000° β=90.00000° γ=120.00000°
Chevrel phase
Mg2Mo6S8
Chemistry of Materials (2006) 18, 23 5492
a=9.7630596(10)Å b=9.7630596(10)Å c=10.3689375(10)Å
α=90.00000° β=90.00000° γ=120.00000°
Chevrel phase
Mo6NaSe8
Inorganic Chemistry (2009) 48, 8751-8758
a=9.572(2)Å b=9.572(2)Å c=11.716(2)Å
α=90.00000° β=90.00000° γ=120.0000°
Chevrel phase
Mo6NaS8
Inorganic Chemistry (2009) 48, 8751-8758
a=9.231(2)Å b=9.231(2)Å c=11.237(2)Å
α=90.00000° β=90.00000° γ=120.0000°
Chevrel phase
Mn3Mo18S24
Inorganic Chemistry (2009) 48, 8751-8758
a=9.467(2)Å b=9.467(2)Å c=10.523(2)Å
α=90.00000° β=90.00000° γ=120.0000°
Chevrel phase
Cd3Mo18S24
Inorganic Chemistry (2009) 48, 8751-8758
a=9.424(2)Å b=9.424(2)Å c=10.750(2)Å
α=90.00000° β=90.00000° γ=120.0000°
Chevrel phase
Cd3Mo18Se24
Inorganic Chemistry (2009) 48, 8751-8758
a=9.793(2)Å b=9.793(2)Å c=11.192(2)Å
α=90.00000° β=90.00000° γ=120.0000°
Chevrel phase
Mo18S24Zn3
Inorganic Chemistry (2009) 48, 8751-8758
a=9.545(2)Å b=9.545(2)Å c=10.296(2)Å
α=90.00000° β=90.00000° γ=120.0000°
Chevrel phase
Mo18Se24Zn3
Inorganic Chemistry (2009) 48, 8751-8758
a=9.910(2)Å b=9.910(2)Å c=10.732(2)Å
α=90.00000° β=90.00000° γ=120.0000°
Chevrel phase
MgMo3Se4
Inorganic Chemistry (2008) 47, 1975-1983
a=6.8781(3)Å b=6.8881(3)Å c=6.9299(3)Å
α=93.030(3)° β=96.230(3)° γ=94.375(4)°
Chevrel phase
Mg3Mo18Se24
Inorganic chemistry (2007) 46, 18 7528-7535
a=9.8489(1)Å b=9.8489(1)Å c=11.0567(2)Å
α=90.00000° β=90.00000° γ=120.00000°
Mg0.75Mo3Se4
Mg0.75Mo3Se4
Inorganic Chemistry (2008) 47, 1975-1983
a=6.868Å b=6.921Å c=6.88Å
α=93° β=94.4° γ=96.22°
CaMn2O4
CaMn2O4
Journal of Alloys and Compounds (2003) 353, 5-11
a=6.2545Å b=9.8995Å c=9.627Å
α=90° β=90° γ=90°
Marokite
CaMn2O4
Journal of Alloys and Compounds (2003) 353, 5-11
a=3.1492Å b=9.98Å c=9.66Å
α=90° β=90° γ=90°
Al0.384D2.759Mn1.616Zr
Al0.384D2.759Mn1.616Zr
Zeitschrift fur Physikalische Chemie (1993) 179, 187-198
a=5.399Å b=5.399Å c=8.828Å
α=90° β=90° γ=120°
D3.396Fe23.17Ho1.914
D3.396Fe23.17Ho1.914
Journal of the Less-Common Metals (1990) 162, 273-284
a=8.499Å b=8.499Å c=8.310Å
α=90° β=90° γ=120°
Fe3Ge3Y0.5
Fe3Ge3Y0.5
Journal of Alloys and Compounds (1998) 267, 59-65
a=8.11975Å b=17.72995Å c=5.11821Å
α=90° β=90° γ=90°
D5.699Mn3.316Ni0.684Zr2
D5.699Mn3.316Ni0.684Zr2
Zeitschrift fur Physikalische Chemie (1993) 179, 187-198
a=5.371Å b=5.371Å c=8.729Å
α=90° β=90° γ=120°